POLYMER SOLUTIONS
PA 1101
Material Data Sheet
PA 1101
Product Description
PA 1101 is a PA 11 based powder for processing in laser sintering systems. The whitish, slightly translucent, additively manufactured parts are characterized by high impact resistance and elongation at break. They do not splinter even under high mechanical loads.
PA 1101 is a bio-based material made from castor oil with a lower CO2e footprint compared to petroleum-based polymers. PA 1101 is therefore also available as a climate-neutral version, the EOS Responsible Product PA 1101 ClimateNeutral. PA 1101 ClimateNeutral combines climate neutrality with the well-known technical properties of PA 1101.
- High ductility
- High impact resistance
- Balanced property profile
- Biobased material
- Impact-resistant applications, which may not splinter when applied with a load, e.g. coverings or housings
- Functional parts that require a high elongation at break, e.g. hinges, clips, or buckles
- Eyewear in the consumer goods industry
| MECHANICAL PROPERTIES | DRY / CONDITIONED | UNIT | TEST STANDARD |
|---|---|---|---|
|
Tensile Modulus X Orientation Y Orientation Z Orientation |
1650 / - 1650 / - 1650 / - |
MPa MPa MPa |
ISO 527-1/-2 |
|
Tensile Strength X Orientation Y Orientation Z Orientation |
50 / - 50 / - 48 / - |
MPa MPa MPa |
ISO 527-1/-2 |
|
Nominal Strain at Break X Orientation Y Orientation Z Orientation |
30 / - 30 / - 15 / - |
% % % |
ISO 527-1/-2 |
|
Nominal Strain at Break, FORMIGA
P 110 Velocis Z Orientation |
22 / - |
% |
ISO 527-1/-2 |
|
Nominal Strain at Break, EOS
P 770 Z Orientation |
12 / - |
% |
ISO527-1/-2 |
|
Charpy Impact Strength (+23°C) X Orientation Y Orientation Z Orientation |
N / - N / - 85 / - |
kJ/m² kJ/m² kJ/m² |
ISO 179/1eU |
|
Charpy Impact Strength (+23°C), FORMIGA
P 110 Velocis Z Orientation |
N / - |
kJ/m² |
ISO 179/1eU |
|
Charpy Impact Strength (-30°C) X Orientation Y Orientation Z Orientation |
N / - N / - 70 / - |
kJ/m² kJ/m² kJ/m² |
ISO 179/1eU |
|
Charpy Impact Strength (-30°C), FORMIGA
P 110 Velocis Z Orientation |
N / - |
% |
ISO 179/1eU |
|
Charpy Notched Impact Strength (+23°C) X Orientation Y Orientation Z Orientation |
6.9 / - 7.3 / - 5.5 / - |
kJ/m² kJ/m² kJ/m² |
ISO 179/1eA |
|
Charpy Notched Impact Strength (-30°C) X Orientation Y Orientation Z Orientation |
6.3 / - 5.8 / - 5.1 / - |
kJ/m² kJ/m² kJ/m² |
ISO 179/1eA |
|
Shore D Hardness X Orientation |
75 / - |
- |
ISO 7619-1 |
| THERMAL PROPERTIES | DRY / CONDITIONED | UNIT | TEST STANDARD |
|---|---|---|---|
| Melting Temperature | 201 | °C | ISO 11357-1/-3 |
|
Temperature of Deflection under Load 1.80 MPa X Orientation Y Orientation Z Orientation |
46 46 47 |
°C °C °C |
ISO 75-1/-2 |
|
Temperature of Deflection under Load 0.45 MPa X Orientation Y Orientation Z Orientation |
180 180 181 |
°C °C °C |
ISO 75-1/-2 |
| ELECTRICAL PROPERTIES | DRY / CONDITIONED | UNIT | TEST STANDARD |
|---|---|---|---|
|
Comparative Tracking Index CTI X Orientation Y Orientation Z Orientation |
≥600 / - ≥600 / - ≥600 / - |
|
IEC 60112 |
| OTHER PROPERTIES | VALUE | UNIT | TEST STANDARD |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183-1 |
| Powder Color | white | - | - |
| Components Color | natural | - | - |