Process Data Sheet
EOS Titanium Ti64 for EOS M 290 | 30 µm
EOS M 290 - 30 µm
| System Setup | EOS M 290 |
|---|---|
| EOS Material set | Ti64_Performance_M291 |
| Software Requirements |
EOSPRINT 1.5 or newer EOSSYTEM 2.4 or newer |
| Recoater Blade | HSS (High Speed Steel) |
| Inert gas | Argon |
| Sieve | 63 µm |
| Additional Information | |
|---|---|
| Layer Thickness | 30 µm |
| Volume Rate | 5 mm³/s |
| Min. Wall Thickness | 0.3 - 0.4 mm |
Microstructure of the Produced Parts
| Density EN ISO 3369 | Thickness | Result | Number of Samples |
|---|---|---|---|
| Average Density | 30 µm | ≥ 4.4 g/cm³ | - |
Mechanical Properties
Mechanical Properties Heat Treated
| EN ISO 6892-1 Room Temperature | 30 µm | Yield Strength [MPa] | Tensile Strength [MPa] | Elongation at Break A [%] | Reduction of Area Z [%] | Modulus of elasticity [GPa] | Number of Samples |
|---|---|---|---|---|---|---|
| Vertical | 965 | 1075 | 14 | 25 | - | - |
| Horizontal | 945 | 1055 | 13 | 25 | - | - |
Reduction of area, Z: >25%
Specimens were heat treated at 800 °C for 2 hours in argon inert atmosphere.
Hardness
| EN ISO 6507 As Manufactured | |
|---|---|
| Value | 320 |
| Unit | HV5 |
Surface roughness
ISO 4287 As Manufactured |
|
|---|---|
| Value |
Ra 9 - 12 µm, Rz 40 - 80 µm |