Process Data Sheet
EOS Titanium Ti64 for EOS M 290 | 60 µm
EOS M 290 - 60 µm
| System Setup | EOS M 290 |
|---|---|
| EOS Material set | Ti64_Speed |
| Recoater Blade | HSS (High Speed Steel) |
| Inert gas | Argon |
| Sieve | 63 µm |
| Additional Information | |
|---|---|
| Layer Thickness | 60 µm |
| Volume Rate | 9 mm³/s |
| Min. Wall Thickness | 0.3 – 0.4 mm |
Microstructure of the Produced Parts
| Defects | Thickness | Result | Number of Samples |
|---|---|---|---|
| Average Defect Percentage | 60 µm | 0.01 % | - |
| Density EN ISO 3369 | Thickness | Result | Number of Samples |
|---|---|---|---|
| Average Density | 60 µm | ≥ 4.4 g/cm³ | - |
Mechanical Properties
Mechanical Properties As Manufactured
| EN ISO 6892-1 Room Temperature | 60 µm | Yield Strength [MPa] | Tensile Strength [MPa] | Elongation at Break A [%] | Reduction of Area Z [%] | Modulus of elasticity [GPa] | Number of Samples |
|---|---|---|---|---|---|---|
| Vertical | 1120 | 1240 | 10 | - | 110 | - |
| Horizontal | 1140 | 1290 | 7 | - | 110 | - |
Mechanical Properties Heat Treated
| EN ISO 6892-1 Room Temperature | 60 µm | Yield Strength [MPa] | Tensile Strength [MPa] | Elongation at Break A [%] | Reduction of Area Z [%] | Modulus of elasticity [GPa] | Number of Samples |
|---|---|---|---|---|---|---|
| Vertical | 1000 | 1100 | 14.5 | - | 110 | - |
| Horizontal | 1000 | 1100 | 13.5 | - | 110 | - |
Specimens were treated at 800 °C (1470 °F) for 4 hours in argon inert atmosphere. Mechanical properties are expressed as minimum values to indicate that mechanical properties exceed the minimum requirements of material specification standards. ASTM F1472-08. By fulfilling these minimum values, also the specifications of standards ASTM B348-09 and ISO 5832-3:2000 are meet.
Hardness
| EN ISO 6507 As Manufactured | |
|---|---|
| Value | 320 |
| Unit | HV5 |