Process Data Sheet
EOS Titanium Ti64 for EOS M 400-4 | 60 µm
EOS M 400-4 - 60 µm
| System Setup | EOS M 400-4 |
|---|---|
| EOS Material set | Ti64_060_FlexM404 |
| Software Requirements |
EOSPRINT 1.6 or higher EOSYSTEM 2.6 or higher |
| Recoater Blade | HSS (High Speed Steel) |
| Inert gas | Argon |
| Sieve | 63 µm |
| Additional Information | |
|---|---|
| Layer Thickness | 60 µm |
| Volume Rate | up to 4 x 9.0 mm³/s |
| Min. Wall Thickness | approx. 0.3 - 0.4 mm |
Microstructure of the Produced Parts
| Density EN ISO 6892-1 | Thickness | Result | Number of Samples |
|---|---|---|---|
| Average Density | 60 µm | ≥ 4.4 g/cm³ | - |
Mechanical Properties
Mechanical Properties Heat Treated
| EN ISO 6892-1 Room Temperature | | Yield Strength [MPa] | Tensile Strength [MPa] | Elongation at Break A [%] | Reduction of Area Z [%] | Modulus of elasticity [GPa] | Number of Samples |
|---|---|---|---|---|---|---|
| Vertical | 990 | 1080 | 15 | - | - | - |
| Horizontal | 955 | 1070 | 13 | - | - | - |
Specimens were heat treated at 800 °C for 2 hours in argon inert atmosphere.
Hardness
| EN ISO 6507 As Manufactured | |
|---|---|
| Value | 330 |
| Unit | HV5 |
Surface roughness
ISO 4287 |
|
|---|---|
| Value |
Ra 6 - 15 µm; Rz 30 - 75 µm |