Process Data Sheet
EOS Titanium Ti64ELI for EOS M 400 | 30 µm
EOS M 400 - 30 µm - TRL 7
| System Setup | EOS M 400 |
|---|---|
| EOS Material set | Ti64ELI_030_FlexM400 |
| Software Requirements |
EOSPRINT 1.5 or newer EOSYSTEM 2.4 or newer |
| Recoater Blade | HSS (High Speed Steel) |
| Inert gas | Argon |
| Sieve | 63 µm |
| Additional Information | |
|---|---|
| Layer Thickness | 30 µm |
| Volume Rate | 5 mm³/s |
Microstructure of the Produced Parts
| Density EN ISO 3369 | Thickness | Result | Number of Samples |
|---|---|---|---|
| Average Density | 30 µm | > 4.4 g/cm³ | - |
Mechanical Properties
Mechanical Properties Heat Treated
| EN ISO 6892-1 Room Temperature | 30 µm | Yield Strength [MPa] | Tensile Strength [MPa] | Elongation at Break A [%] | Reduction of Area Z [%] | Modulus of elasticity [GPa] | Number of Samples |
|---|---|---|---|---|---|---|
| Vertical | 1100 | 1270 | 8.7 | - | - | - |
| Horizontal | 1100 | 1270 | 8.7 | - | - | - |
Heat treatment procedure: 2 hours at 800ºC in Argon atmosphere.
The numbers are average values and are determined from samples with horizontal and vertical orientation.
Mechanical Properties Heat Treated
| EN ISO 6892-1 Room Temperature | | Yield Strength [MPa] | Tensile Strength [MPa] | Elongation at Break A [%] | Reduction of Area Z [%] | Modulus of elasticity [GPa] | Number of Samples |
|---|---|---|---|---|---|---|
| Vertical | 930 | 1040 | 14 | - | - | - |
| Horizontal | 930 | 1040 | 14 | - | - | - |
The numbers are average values and are determined from samples with horizontal and vertical orientation.
Hardness
| EN ISO 6507 As Manufactured | |
|---|---|
| Value | 340 |
| Unit | HV5 |
Surface Roughness after shotpeening
| Post-processed | |
|---|---|
| Value |
Ra 5 - 10 µm; Rz 15 - 30 µm |