Process Data Sheet
EOS Titamium TiCP for EOS M 290 | 30 µm
EOS M 290 - 30 µm
| System Setup | EOS M 290 |
|---|---|
| EOS Material set | TiCP 30µm FlexLine |
| Software Requirements |
EOSPRINT 1.3 or newer EOSYSTEM 2.3 or newer |
| Recoater Blade | HSS (High Speed Steel) |
| Inert gas | Argon |
| Sieve | 63 µm |
| Additional Information | |
|---|---|
| Layer Thickness | 30 µm |
| Volume Rate | 5.0 mm³/s |
Microstructure of the Produced Parts
| Density EN ISO 3369 | Thickness | Result | Number of Samples |
|---|---|---|---|
| Average Density | 30 µm | ≥ 4.5 g/cm³ | - |
Mechanical Properties
Mechanical Properties As Manufactured
| EN ISO 6892-1 Room Temperature | 30 µm | Yield Strength [MPa] | Tensile Strength [MPa] | Elongation at Break A [%] | Reduction of Area Z [%] | Modulus of elasticity [GPa] | Number of Samples |
|---|---|---|---|---|---|---|
| Vertical | 560 | 660 | 22 | 30 | - | - |
| Horizontal | 560 | 660 | 22 | 30 | - | - |
The numbers are average values and are determined from samples with horizontal and vertical orientation.
The numbers are average values and are determined from samples with horizontal and vertical orientation.
Mechanical Properties Heat Treated
| EN ISO 6892-1 Room Temperature | 30 µm | Yield Strength [MPa] | Tensile Strength [MPa] | Elongation at Break A [%] | Reduction of Area Z [%] | Modulus of elasticity [GPa] | Number of Samples |
|---|---|---|---|---|---|---|
| Vertical | 445 | 570 | 26 | 30 | - | - |
| Horizontal | 445 | 570 | 26 | 30 | - | - |
Heat treatment in 700 °C (± 10 °C) for 2 h (± 0.5 h) under argon.
The numbers are average values and are determined from samples with horizontal and vertical orientation.
The numbers are average values and are determined from samples with horizontal and vertical orientation.
Hardness
| EN ISO 6507 Heat Treated | |
|---|---|
| Value | 195 |
| Unit | HV5 |
Surface roughness after shot peening
| Post-processed | |
|---|---|
| Value |
Ra < 10 µm; Rz < 55 µm |