PA 2200 CarbonReduced Balance

Process Data Sheet

Process Information Polymer

Product Description

The advantage of the process parameter Balance, at 120µm layer thickness, lies in its ability to balance different factors at the same time, e.g., production costs, mechanical properties, surface quality and accuracy. Therefore it is suitable for parts with varying geometries, dimensions and requirements.

MECHANICAL PROPERTIES	DRY / CONDITIONED	UNIT	TEST STANDARD
Tensile Modulus X Orientation Y Orientation Z Orientation	1650 / - 1650 / - 1650 / -	MPa MPa MPa	ISO 527-1/-2
Tensile Strength X Orientation Y Orientation Z Orientation	48 / - 48 / - 42 / -	MPa MPa MPa	ISO 527-1/-2
Nominal Strain at Break X Orientation Y Orientation Z Orientation	18 / - 18 / - 4 / -	% % %	ISO 527-1/-2
Flexural Modulus X Orientation	1500 / -	MPa	ISO 178
Charpy Impact Strength (+23°C) X Orientation	53 / -	kJ/m²	ISO 179/1eU
Charpy Notched Impact Strength (+23°C) X Orientation	4.8 / -	kJ/m²	ISO 179/1eA
Izod Notched Impact Strength (+23°C) X Orientation	4.4 / -	kJ/m²	ISO 180/1A
Shore D Hardness X Orientation	75 / -	-	ISO 7619-1

THERMAL PROPERTIES	DRY / CONDITIONED	UNIT	TEST STANDARD
Melting Temperature	176	°C	ISO 11357-1/-3
Temperature of Deflection under Load 1.80 MPa X Orientation Z Orientation	64 57	°C °C	ISO 75-1/-2
Temperature of Deflection under Load 0.45 MPa X Orientation Z Orientation	157 145	°C °C	ISO 75-1/-2
Vicat Softening Temperature X Orientation	176	°C	ISO 306/B50
Burning Behavior Thickness Tested	HB 0.5	class mm	UL 94
Burning Behavior Thickness Tested	HB 1.6	class mm	UL 94
Burning Behavior Thickness Tested	HB 3.2	class mm	UL 94

ELECTRICAL PROPERTIES	DRY / CONDITIONED	UNIT	TEST STANDARD
Comparative Tracking Index CTI X Orientation Y Orientation Z Orientation	≥600 / - ≥600 / - ≥600 / -		IEC 60112

OTHER PROPERTIES	VALUE	UNIT	TEST STANDARD
Density	0.93	g/cm³	EOS Method
Powder Color	white	-	-
Components Color	white	-	-