POLYMER SOLUTIONS
PA 2200 CarbonReduced Top Speed
Process Data Sheet
Process Information Polymer
PA 2200 CarbonReduced Top Speed
Product Description
The advantage of the process parameter Top Speed, with 180µm layer thickness, lies in its ability to build parts with medium to high requirements of quality and mechanical load combined with high cost pressure. Particularly large and relatively thick-walled parts can usually profit from this layer thickness, mostly without any noticeable impairment from the fast build-up rates.
| MECHANICAL PROPERTIES | DRY / CONDITIONED | UNIT | TEST STANDARD |
|---|---|---|---|
|
Tensile Modulus X Orientation Y Orientation Z Orientation |
1500 / - 1500 / - 1500 / - |
MPa MPa MPa |
ISO 527-1/-2 |
|
Tensile Strength X Orientation Y Orientation Z Orientation |
45 / - 45 / - 38 / - |
MPa MPa MPa |
ISO 527-1/-2 |
|
Nominal Strain at Break X Orientation Y Orientation Z Orientation |
18 / - 18 / - 3 / - |
% % % |
ISO 527-1/-2 |
|
Shore D Hardness X Orientation |
75 / - |
- |
ISO 7619-1 |
| OTHER PROPERTIES | VALUE | UNIT | TEST STANDARD |
|---|---|---|---|
| Powder Color | white | - | - |
| Components Color | white | - | - |