PA 1102 Black

Material Data Sheet

PA 1102 Black

Product Description

PA 1102 black is a PA 11 based powder for processing in laser sintering systems. The black, additively manufactured parts are characterized by high impact resistance and elongation at break. They do not splinter even under high mechanical loads. Due to the mass-dyed polyamide 11 powder, parts made from PA 1102 black have a uniform black color and are therefore particularly suitable for visible areas that are subject to abrasive wear. As all other PA 11 powders at EOS, PA 1102 black is based on renewable resources (castor oil).

MAIN CHARACTERISTICS

  • Color stability
  • High ductility
  • High impact resistance
  • From renewable sources

TYPICAL APPLICATIONS

  • Impact-resistant applications, which may not splinter when applied with a load, e.g, coverings or housings
  • Functional parts that reuqire a high elongation at break, e.g., clips or buckles
  • Eye wear in the consumer goods industry
MECHANICAL PROPERTIES DRY / CONDITIONED UNIT TEST STANDARD
Tensile Modulus
X Orientation
Y Orientation
Z Orientation

1560 / -
1560 / -
1610 / -

MPa
MPa
MPa
ISO 527-1/-2
Tensile Strength
X Orientation
Y Orientation
Z Orientation

48 / -
48 / -
48 / -

MPa
MPa
MPa
ISO 527-1/-2
Nominal Strain at Break
X Orientation
Y Orientation
Z Orientation

30 / -
30 / -
15 / -

%
%
%
ISO 527-1/-2
Charpy Impact Strength (+23°C)
X Orientation
Y Orientation

N / -
N / -

kJ/m²
kJ/m²
ISO 179/1eU
Charpy Notched Impact Strength (+23°C)
X Orientation
Y Orientation
Z Orientation

7.8 / -
7.8 / -
6.5 / -

kJ/m²
kJ/m²
kJ/m²
ISO 179/1eA
THERMAL PROPERTIES DRY / CONDITIONED UNIT TEST STANDARD
Melting Temperature 201 °C ISO 11357-1/-3
OTHER PROPERTIES VALUE UNIT TEST STANDARD
Density 0.99 g/cm³ EOS Method
Powder Color black - -
Components Color black - -